Enhanced critical current density of MgB2 superconductor synthesized in high magnetic fields

The effect of high magnetic fields on the current carrying properties of both MgB2 bulks and Fe-sheathed tapes was investigated following different thermal sequences. It is found that application of a large magnetic field during processing results in the quite uniform microstructure and the better connectivity between the MgB2 grains. As a result, the Jc of these samples has shown much higher value than that of the MgB2 samples in the absence of magnetic field. The possible mechanism of the Jc enhancement under an external magnetic field is also discussed.Comment: Presented at ISS2005, Tsukuba, 24-26 Oct., 2005; Revised versio

Significantly enhanced critical current densities in MgB2 tapes made by a scaleable, nano-carbon addition route

Nanocarbon-doped Fe-sheathed MgB2 tapes with different doping levels were prepared by the in situ powder-in-tube method. Compared to the undoped tapes, Jc for all the C-doped samples was enhanced by more than an order of magnitude in magnetic fields above 9 T. At 4.2 K, the transport Jc for the 5 at% doped tapes reached 1.85x104 A/cm2 at 10 T and 2.8x103 A/cm2 at 14 T, respectively. Moreover, the critical temperature for the doped tapes decreased slightly. Transmission electron microscopy showed a number of intra-granular dislocations and the dispersed nanoparticles embedded within MgB2 grains induced by the C doping. The mechanism for the enhancement of flux pinning is also discussed. These results indicate that powder-in-tube-processed MgB2 tape is very promising for high-field applications.Comment: 13 pages, 5 figures. to be published soo

Multichannel parametrization of \pi N scattering amplitudes and extraction of resonance parameters

We present results of a new multichannel partial-wave analysis for \pi N scattering in the c.m. energy range 1080 to 2100 MeV. This work explicitly includes \eta N and K \Lambda channels and the single pion photoproduction channel. Resonance parameters were extracted by fitting partial-wave amplitudes from all considered channels using a multichannel parametrization that is consistent with S-matrix unitarity. The resonance parameters so obtained are compared to predictions of quark models