The Effect of Surface Treatments on Zirconia Bond Strength and Durability

To evaluate the effects of airborne particle abrasion (APA) combined with MDP-containing resin cement, a glass-ceramic spray deposition (GCSD) method on the shear bond strengths (SBSs) and durability of 3 mol% yttrium oxide-stabilized zirconia ceramic (3Y-TZP) compared with lithium disilicate glass ceramics (LDGC). 3Y-TZP disks were randomly treated as follows: for Group APA+MDP, 3Y-TZP was abrased using 50 µm Al2O3 particles under 0.1 Mpa and bonded with MDP-containing resin cement; for Group GCSD, 3Y-TZP was treated with the GCSD method, etched by 5% HF for 90 s, silanized and bonded with resin cement without MDP. Group LDGC was bonded as the Group GCSD. X-ray diffraction (XRD), attenuated total reflection Fourier transform infrared spectroscopy (ATR-FTIR), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) and energy dispersive X-ray detector (EDX) were used to analyze the surface chemical and micro-morphological changes of the ceramics before bonding. The bonded ceramic specimens were randomly divided into subgroups, and the SBSs were determined before and after 10,000 thermocycling. The SBSs were analyzed with a one-way ANOVA analysis. Failure modes were determined with optical microscopy and SEM. The XRD, ATR-FTIR and XPS results identified the formation of lithium disilicate and zirconium silicate on 3Y-TZP after GCSD. The SEM micrographs revealed that 3Y-TZP surfaces were roughened by APA, while 3Y-TZP with GCSD and LDGC surfaces could be etched by HF to be porous. The APA treatment combined with MDP-containing resin cement produced the high immediate zirconia shear bond strengths (SBSs: 37.41 ± 13.51 Mpa) that was similar to the SBSs of the LDGC (34.87 ± 11.02 Mpa, p > 0.05), but, after thermocycling, the former dramatically decreased (24.00 ± 6.86 Mpa, maximum reduction by 35.85%) and the latter exhibited the highest SBSs (30.72 ± 7.97 Mpa, minimum reduction by 11.9%). The 3Y-TZP with GCSD treatment displayed the lower zirconia SBSs before thermocycling (27.03 ± 9.76 Mpa, p < 0.05), but it was similar to the 3Y-TZP treated with APA and MDP containing resin cement after thermocycling (21.84 ± 7.03 vs. 24.00 ± 6.86 Mpa, p > 0.05). The APA combined with MDP-containing resin cement could achieve the high immediate zirconia SBSs of those of the LDGC, but it decreased significantly after thermocycling. The GCSD technique could yield the immediate zirconia SBSs similar to those of LDGC before thermocycling, and long-term zirconia SBSs were similar to those of 3Y-TZP treated with APA followed by MDP-containing resin cement after thermocycling. Hence, the GCSD technique could enrich zirconia surface treatments and is an alternative to zirconia surface pretreatment for 3Y-TZP bond durability

Plasma D-dimer and prothrombin fragment 1+2 in evaluating the occurrence of venous thromboembolism in advanced cancer patients and the effect of preventive anticoagulant therapy

Background: This study aimed to evaluate the role of D-dimer (DD) and prothrombin fragment 1+2 (PF1+2) in assessing the risk of venous thromboembolism (VTE) in advanced cancer patients, as well as the impact of preventive anticoagulant therapy. Methods: A total of 137 advanced cancer patients admitted to the 908th Hospital of the Chinese People's Liberation Army Joint Logistic Support Force Hospital between February 2023 and June 2024 were included. Patients were divided into two groups based on the presence (VTE group, n=49) or absence (non-VTE group, n=88) of VTE. Blood tests were performed at admission, and the relationship between DD, PF1+2, and VTE risk was analysed. Patients without VTE were further categorised into two treatment groups: the preventive anticoagulant treatment group (AG, n=48) and the conventional treatment group (RT, n=40), based on their preference. The incidence of VTE in both groups was compared to assess the effectiveness of preventive anticoagulant therapy. Results: Before chemotherapy, DD levels were significantly higher in patients who developed VTE than those who did not. Both DD and PF1+2 were found to be independent risk factors for VTE after chemotherapy. The incidence of VTE was lower in the AG group than in the RT group, with a statistically significant difference. Conclusions: DD and PF1+2 are reliable indicators for assessing VTE risk in advanced cancer patients and can help guide the use of preventive anticoagulant therapy

Influence of needle working length and root canal curvature on irrigation: a computational fluid dynamics analysis based on a real tooth

Abstract Backgrounds To compare the irrigation efficiency with different needle working length and different root canal curvature based on a real unshaped root canal using computational fluid dynamics (CFD) method. Methods Images of the root canal of the maxillary first molar after being prepared to .04/15 were scanned using micro-CT, and then imported into the software for three-dimensional reconstruction. A palatal root canal with a curvature of 23.4° was selected as the experiment canal. The needle working length of the 30-G flat needle was 4.75 mm, 5 mm, 5.25 mm and 5.5 mm short of apical foramen respectively, the flow pattern, irrigation velocity, shear stress were compared. The modified curved canals with a curvature of 0°, 5°, 10°, 20° and 30°were reconstructed via software. The flat needle was replaced at the optical inserted depth, and key parameters of irrigation efficiency were analyzed. Results Decreased needle working length had a positive impact on irrigation efficiency. With the optimal needle working length, the replacement of the apical irrigation fluid, the effective velocity, and wall shear stress were significantly improved in more severely curved root canals. With the same needle working depth and analogous canal curvature, irrigation efficiency is higher in real canal than that of modified canal. Conclusions Short needle working depth, large curvature and the anomalous inner wall of canals help to improve irrigation efficiency. </jats:sec

The Effect of Surface Treatments on Zirconia Bond Strength and Durability

To evaluate the effects of airborne particle abrasion (APA) combined with MDP-containing resin cement, a glass-ceramic spray deposition (GCSD) method on the shear bond strengths (SBSs) and durability of 3 mol% yttrium oxide-stabilized zirconia ceramic (3Y-TZP) compared with lithium disilicate glass ceramics (LDGC). 3Y-TZP disks were randomly treated as follows: for Group APA+MDP, 3Y-TZP was abrased using 50 &mu;m Al2O3 particles under 0.1 Mpa and bonded with MDP-containing resin cement; for Group GCSD, 3Y-TZP was treated with the GCSD method, etched by 5% HF for 90 s, silanized and bonded with resin cement without MDP. Group LDGC was bonded as the Group GCSD. X-ray diffraction (XRD), attenuated total reflection Fourier transform infrared spectroscopy (ATR-FTIR), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) and energy dispersive X-ray detector (EDX) were used to analyze the surface chemical and micro-morphological changes of the ceramics before bonding. The bonded ceramic specimens were randomly divided into subgroups, and the SBSs were determined before and after 10,000 thermocycling. The SBSs were analyzed with a one-way ANOVA analysis. Failure modes were determined with optical microscopy and SEM. The XRD, ATR-FTIR and XPS results identified the formation of lithium disilicate and zirconium silicate on 3Y-TZP after GCSD. The SEM micrographs revealed that 3Y-TZP surfaces were roughened by APA, while 3Y-TZP with GCSD and LDGC surfaces could be etched by HF to be porous. The APA treatment combined with MDP-containing resin cement produced the high immediate zirconia shear bond strengths (SBSs: 37.41 &plusmn; 13.51 Mpa) that was similar to the SBSs of the LDGC (34.87 &plusmn; 11.02 Mpa, p &gt; 0.05), but, after thermocycling, the former dramatically decreased (24.00 &plusmn; 6.86 Mpa, maximum reduction by 35.85%) and the latter exhibited the highest SBSs (30.72 &plusmn; 7.97 Mpa, minimum reduction by 11.9%). The 3Y-TZP with GCSD treatment displayed the lower zirconia SBSs before thermocycling (27.03 &plusmn; 9.76 Mpa, p &lt; 0.05), but it was similar to the 3Y-TZP treated with APA and MDP containing resin cement after thermocycling (21.84 &plusmn; 7.03 vs. 24.00 &plusmn; 6.86 Mpa, p &gt; 0.05). The APA combined with MDP-containing resin cement could achieve the high immediate zirconia SBSs of those of the LDGC, but it decreased significantly after thermocycling. The GCSD technique could yield the immediate zirconia SBSs similar to those of LDGC before thermocycling, and long-term zirconia SBSs were similar to those of 3Y-TZP treated with APA followed by MDP-containing resin cement after thermocycling. Hence, the GCSD technique could enrich zirconia surface treatments and is an alternative to zirconia surface pretreatment for 3Y-TZP bond durability

The Effect of Surface Treatments on Zirconia Bond Strength and Durability

To evaluate the effects of airborne particle abrasion (APA) combined with MDP-containing resin cement, a glass-ceramic spray deposition (GCSD) method on the shear bond strengths (SBSs) and durability of 3 mol% yttrium oxide-stabilized zirconia ceramic (3Y-TZP) compared with lithium disilicate glass ceramics (LDGC). 3Y-TZP disks were randomly treated as follows: for Group APA+MDP, 3Y-TZP was abrased using 50 μm Al2O3 particles under 0.1 Mpa and bonded with MDP-containing resin cement; for Group GCSD, 3Y-TZP was treated with the GCSD method, etched by 5% HF for 90 s, silanized and bonded with resin cement without MDP. Group LDGC was bonded as the Group GCSD. X-ray diffraction (XRD), attenuated total reflection Fourier transform infrared spectroscopy (ATR-FTIR), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) and energy dispersive X-ray detector (EDX) were used to analyze the surface chemical and micro-morphological changes of the ceramics before bonding. The bonded ceramic specimens were randomly divided into subgroups, and the SBSs were determined before and after 10,000 thermocycling. The SBSs were analyzed with a one-way ANOVA analysis. Failure modes were determined with optical microscopy and SEM. The XRD, ATR-FTIR and XPS results identified the formation of lithium disilicate and zirconium silicate on 3Y-TZP after GCSD. The SEM micrographs revealed that 3Y-TZP surfaces were roughened by APA, while 3Y-TZP with GCSD and LDGC surfaces could be etched by HF to be porous. The APA treatment combined with MDP-containing resin cement produced the high immediate zirconia shear bond strengths (SBSs: 37.41 ± 13.51 Mpa) that was similar to the SBSs of the LDGC (34.87 ± 11.02 Mpa, p &gt; 0.05), but, after thermocycling, the former dramatically decreased (24.00 ± 6.86 Mpa, maximum reduction by 35.85%) and the latter exhibited the highest SBSs (30.72 ± 7.97 Mpa, minimum reduction by 11.9%). The 3Y-TZP with GCSD treatment displayed the lower zirconia SBSs before thermocycling (27.03 ± 9.76 Mpa, p &lt; 0.05), but it was similar to the 3Y-TZP treated with APA and MDP containing resin cement after thermocycling (21.84 ± 7.03 vs. 24.00 ± 6.86 Mpa, p &gt; 0.05). The APA combined with MDP-containing resin cement could achieve the high immediate zirconia SBSs of those of the LDGC, but it decreased significantly after thermocycling. The GCSD technique could yield the immediate zirconia SBSs similar to those of LDGC before thermocycling, and long-term zirconia SBSs were similar to those of 3Y-TZP treated with APA followed by MDP-containing resin cement after thermocycling. Hence, the GCSD technique could enrich zirconia surface treatments and is an alternative to zirconia surface pretreatment for 3Y-TZP bond durability.</jats:p