Bending properties of finger-jointed Malaysian dark red meranti

The mechanical performance of dark red meranti (Shorea spp.) containing structural finger joints was investigated in four-point bending. The influence of variation in density on the bending strength (MOR) and stiffness (MOE) of dark red meranti (DRM) was studied. The effect on these properties of variation in end pressure when bonding was examined. The orientation of finger joints and the effect of cross-sectional area of bonded joints on the bending properties were also investigated. The results of this study indicate a positive relationship between the density and the MOR of DRM specimens. Sufficiently high end pressure is needed to produce strong finger joints. The orientation of finger joints and the changes in cross-sectional area of bonded joints showed no influence on the MOR. The MOE of DRM was not affected by the finger jointing of the pieces. In conclusion, finger-jointed DRM exhibits potential for structural uses, particularly for glulam beams

Impregnation of Bombax ceiba and Bombax insigne wood with a N-methylol melamine compound

Methylated N-methylol melamine (NMM) is known for its ability to enhance physico-mechanical properties, anti-fungal ability, and hydrophobicity and was therefore used to impregnate two less used and non-durable wood species from Myanmar, Bombax ceiba and Bombax insigne. Solution uptake, weight percent gain and nitrogen content were increased by increasing melamine concentrations with B. ceiba always achieving higher values compared with B. insigne. According to the leaching results, a higher degree of condensation after curing as well as a better crosslinking of NMM could be obtained at higher temperatures. However, both curing temperatures used (90 and 120 A degrees C) resulted in almost the same amount of nitrogen fixed in the cell wall. UV microspectrophotometry confirmed the penetration of the NMM into different morphological regions of wood tissues, which was again supported by the analysis of point measurement spectra of treated and untreated specimens