Effect of high-pressure torsion on microstructure, mechanical properties and corrosion resistance of cast pure Mg

© 2018, The Author(s). High-pressure torsion (HPT) processing was applied to cast pure magnesium, and the effects of the deformation on the microstructure, hardness, tensile properties and corrosion resistance were evaluated. The microstructures of the processed samples were examined by electron backscatter diffraction, and the mechanical properties were determined by Vickers hardness and tensile testing. The corrosion resistance was studied using electrochemical impedance spectroscopy in a 3.5% NaCl solution. The results show that HPT processing effectively refines the grain size of Mg from millimeters in the cast structure to a few micrometers after processing and also creates a basal texture on the surface. It was found that one or five turns of HPT produced no significant difference in the grain size of the processed Mg and the hardness was a maximum after one turn due to recovery in some grains. Measurements showed that the yield strength of the cast Mg increased by about seven times whereas the corrosion resistance was not significantly affected by the HPT processing

Parameter optimization in milling of glass fiber reinforced plastic (GFRP) using DOE-Taguchi method

Introduction: Optimization of machining parameters is essential for improving expected outcome of any machining operation. Case Description: The aim of this work is to find out optimum values of machining parameters to achieve minimal surface roughness during milling operation of GFRP. Discussion and Evaluation: In this machining operation speed, depth of cut and feed rate are considered as parameters affecting surface roughness and Design of Experiment (DOE)-Taguchi method tool is used to plan experiments and analyse results. Conclusion: Analysis of experimental results presents optimum values of these three parameters to achieve minimal surface roughness with speed as a major contributing factor. Speed—200 rpm, depth of cut—1.2 mm and feed—40 mm/min are an optimal combination of machining parameter to produce minimal surface roughness during milling of GFRP

Potential therapeutic applications of microbial surface-activecompounds

Numerous investigations of microbial surface-active compounds or biosurfactants over the past two decades have led to the discovery of many interesting physicochemical and biological properties including antimicrobial, anti-biofilm and therapeutic among many other pharmaceutical and medical applications. Microbial control and inhibition strategies involving the use of antibiotics are becoming continually challenged due to the emergence of resistant strains mostly embedded within biofilm formations that are difficult to eradicate. Different aspects of antimicrobial and anti-biofilm control are becoming issues of increasing importance in clinical, hygiene, therapeutic and other applications. Biosurfactants research has resulted in increasing interest into their ability to inhibit microbial activity and disperse microbial biofilms in addition to being mostly nontoxic and stable at extremes conditions. Some biosurfactants are now in use in clinical, food and environmental fields, whilst others remain under investigation and development. The dispersal properties of biosurfactants have been shown to rival that of conventional inhibitory agents against bacterial, fungal and yeast biofilms as well as viral membrane structures. This presents them as potential candidates for future uses in new generations of antimicrobial agents or as adjuvants to other antibiotics and use as preservatives for microbial suppression and eradication strategies

Studying the Microstructural Effect of Selective Laser Melting and Electropolishing on the Performance of Maraging Steel

AbstractSelective laser melting is one of the additive manufacturing technologies that have been known for building various and complicated shapes. Despite numerous advantages of additive manufacturing technologies, they strongly influence the microstructure and typically show a relatively high surface roughness. In this study, maraging steel was produced by selective laser melting (SLM), and its microstructure, hardness and corrosion behavior before and after heat treatment were studied and compared to traditionally manufactured ones (wrought, forged samples). In addition, the effect of electropolishing on the surface roughness was evaluated. The microstructural study was carried out by scanning electron microscopy equipped with electron backscattered diffraction in three different sections: parallel to the top surface (xy), transverse cross section (xz) and longitudinal cross section (yz). The same characterization was applied to heat-treated samples, austenitized and quenched as well as the aged ones. The results showed that selective laser melting produced a fine grain martensitic structure (in the as-printed condition) with a surface roughness (Ra) of about 10 µm. There was no sign of preferred texture or anisotropy in the microstructure of as-print SLM materials. The SLM microstructure was similar in all 3 sections (xy, xz and yz). Despite finer microstructure, nano-hardness and corrosion behavior of SLM and conventional wrought maraging steel in heat-treated conditions were similar. Aging resulted in the maximum nano-hardness and the minimum corrosion potential values. Precipitation has the main role in both hardness and corrosion behavior. Electropolishing was optimized and reduced the surface roughness (Ra) by 65%.</jats:p

Studying the microstructural effect of selective laser melting and electropolishing on the performance of maraging steel

Selective laser melting is one of the additive manufacturing technologies that have been known for building various and complicated shapes. Despite numerous advantages of additive manufacturing technologies, they strongly influence the microstructure and typically show a relatively high surface roughness. In this study, maraging steel was produced by selective laser melting (SLM), and its microstructure, hardness and corrosion behavior before and after heat treatment were studied and compared to traditionally manufactured ones (wrought, forged samples). In addition, the effect of electropolishing on the surface roughness was evaluated. The microstructural study was carried out by scanning electron microscopy equipped with electron backscattered diffraction in three different sections: parallel to the top surface (xy), transverse cross section (xz) and longitudinal cross section (yz). The same characterization was applied to heat-treated samples, austenitized and quenched as well as the aged ones. The results showed that selective laser melting produced a fine grain martensitic structure (in the as-printed condition) with a surface roughness (Ra) of about 10 µm. There was no sign of preferred texture or anisotropy in the microstructure of as-print SLM materials. The SLM microstructure was similar in all 3 sections (xy, xz and yz). Despite finer microstructure, nano-hardness and corrosion behavior of SLM and conventional wrought maraging steel in heat-treated conditions were similar. Aging resulted in the maximum nano-hardness and the minimum corrosion potential values. Precipitation has the main role in both hardness and corrosion behavior. Electropolishing was optimized and reduced the surface roughness (Ra) by 65%.Open access funding provided by Jönköping University.http://link.springer.com/journal/11665hj2021Materials Science and Metallurgical Engineerin

Study of the effect of pulse plating parameters on the electrodeposition of NiP and NiP/SiC coatings and their microhardness values

This study is focused on finding optimised conditions for electrodeposition of NiP and NiP/SiC coatings, which enhance the coatings' microhardness. Both the effect of particles and the effect of heat treatment at 400°C for 1 h on the microhardness of the coating were studied. The effects of pulse electrodeposition parameters including duty cycle, frequency, and peak current density on the composition of NiP and NiP/SiC composite coatings were examined, and the results were compared with those from direct current plating. Pulse plating increased the current efficiency of NiP deposition while decreasing the phosphorus content of these coatings in comparison to direct plating, resulting in higher microhardness values. It was also shown that wt.%P in NiP coating depends not only on peak current density but also on bath charge of pulse plating. Pulse plating parameters (duty cycle and frequency) and the low incorporation of SiC particles did not affect microstructure or the microhardness of the coatings, while heat treatment was the main factor that increased microhardness.</p