Contact angle measurements of a polyphenyl ether to 190 C on M-50 steel

Contact angle measurements were performed for a polyphenyl ether on steel in nitrogen. A tilting plate and a sessile drop apparatus were used. Surface tension was measured with a maximum bubble pressure apparatus. Critical surface energies of spreading were found to be 30.1 and 31.3 dynes/cm. It was concluded that the polyphenyl ether is inherently autophobic and will not spread on its own surface film

Tribological measurements on a Charnley-type artificial hip joint

A total hip simulator was used to determine the friction and wear properties of Charnley-type (316L stainless steel balls and sterile ultrahigh molecular weight polyethylene cups) hip prostheses. Three different sets of specimens were tested to 395,000, 101,500 and 233,000 walking cycles, respectively. All tests were run unlubricated, at ambient conditions (22 to 26 C, 30 to 50 percent relative humidity), at 30 walking cycles per minute, under a dynamic load simulating walking. Polyethylene cup wear rates ranged from 1.4 to 39 ten billions cu m which corresponds to dimensional losses of 4.0 to 11 microns per year. Although these wear rates are lower than those obtained from other hip simulators and from in vivo X-ray measurements, they are comparable when taking run-in and plastic deformation into account. Maximum tangential friction forces ranged from 93 to 129 N under variable load (267 to 3090 N range) and from 93 to 143 N under a static load of 3090 N. A portion of one test 250,000 walking cycles) run under dry air ( 1 percent relative humidity) yielded a wear rate almost 6 times greater than that obtained under wet air ( 70 percent relative humidity) conditions

Elucidation of wear mechanisms by ferrographic analysis

The use of ferrographic analysis in conjunction with light and scanning electron microscopy is described for the elucidation of wear mechanisms taking place in operating equipment. Example of adhesive wear, abrasive wear, corrosive wear, rolling element fatigue, lubricant breakdown, and other wear modes are illustrated. In addition, the use of magnetic solutions to precipitate nonmagnetic debris from aqueous and nonaqueous fluids is described

Ferrographic and spectrometer oil analysis from a failed gas turbine engine

An experimental gas turbine engine was destroyed as a result of the combustion of its titanium components. It was concluded that a severe surge may have caused interference between rotating and stationary compressor that either directly or indirectly ignited the titanium components. Several engine oil samples (before and after the failure) were analyzed with a Ferrograph, a plasma, an atomic absorption, and an emission spectrometer to see if this information would aid in the engine failure diagnosis. The analyses indicated that a lubrication system failure was not a causative factor in the engine failure. Neither an abnormal wear mechanism nor a high level of wear debris was detected in the engine oil sample taken just prior to the test in which the failure occurred. However, low concentrations (0.2 to 0.5 ppm) of titanium were evident in this sample and samples taken earlier. After the failure, higher titanium concentrations ( 2 ppm) were detected in oil samples taken from different engine locations. Ferrographic analysis indicated that most of the titanium was contained in spherical metallic debris after the failure. The oil analyses eliminated a lubrication system bearing or shaft seal failure as the cause of the engine failure

Theoretical and subjective bit assignments in transform picture

It is shown that all combinations of symmetrical input distributions with difference distortion measures give a bit assignment rule identical to the well-known rule for a Gaussian input distribution with mean-square error. Published work is examined to show that the bit assignment rule is useful for transforms of full pictures, but subjective bit assignments for transform picture coding using small block sizes are significantly different from the theoretical bit assignment rule. An intuitive explanation is based on subjective design experience, and a subjectively obtained bit assignment rule is given

EMPIRICAL SUCCESS RATIOS IN USDA AGRICULTURAL UTILIZATION RESEARCH

Research Methods/ Statistical Methods,

Ferrographic and spectrographic analysis of oil sampled before and after failure of a jet engine

An experimental gas turbine engine was destroyed as a result of the combustion of its titanium components. Several engine oil samples (before and after the failure) were analyzed with a Ferrograph as well as plasma, atomic absorption, and emission spectrometers. The analyses indicated that a lubrication system failure was not a causative factor in the engine failure. Neither an abnormal wear mechanism, nor a high level of wear debris was detected in the oil sample from the engine just prior to the test in which the failure occurred. However, low concentrations of titanium were evident in this sample and samples taken earlier. After the failure, higher titanium concentrations were detected in oil samples taken from different engine locations. Ferrographic analysis indicated that most of the titanium was contained in spherical metallic debris after the failure

Boundary lubrication: Revisited

A review of the various lubrication regimes, with particular, emphasis on boundary lubrication, is presented. The types of wear debris and extent of surface damage is illustrated for each regime. The role of boundary surface films along with their modes of formation and important physical properties are discussed. In addition, the effects of various operating parameters on friction and wear in the boundary lubrication regime are considered

Wear particle analysis using the ferrograph

The use of the Ferrograph in analyzing wear particles from a variety of different sources is reported. Examples of wear particles from gas turbine engines, bearing tests, friction and wear tests, hydraulic systems, and human joints are illustrated. In addition, the separation of bacteria and human cells is described