Deep flaws in weldments of aluminum and titanium

Surface flawed specimens of 2219-T87 and 6Al-4V STA titanium weldments were tested to determine static failure modes, failure strength, and fatigue flaw growth characteristics. Thicknesses selected for this study were purposely set at values where, for most test conditions, abrupt instability of the flaw at fracture would not be expected. Static tests for the aluminum weldments were performed at room, LN2 and LH2 temperatures. Titanium static tests for tests were performed at room and LH2 temperatures. Results of the static tests were used to plot curves relating initial flaw size to leakage- or failure-stresses (i.e. "failure" locus curves). Cyclic tests, for both materials, were then performed at room temperature, using initial flaws only slightly below the previously established failure locus for typical proof stress levels. Cyclic testing was performed on pairs of specimens, one with and one without a simulated proof test cycle. Comparisons were made then to determine the value and effect of proof testing as affected by the various variables of proof and operating stress, flaw shape, material thickness, and alloy

Buckling without bending: a new paradigm in morphogenesis

A curious feature of organ and organoid morphogenesis is that in certain cases, spatial oscillations in the thickness of the growing "film" are out-of-phase with the deformation of the slower-growing "substrate," while in other cases, the oscillations are in-phase. The former cannot be explained by elastic bilayer instability, and contradict the notion that there is a universal mechanism by which brains, intestines, teeth, and other organs develop surface wrinkles and folds. Inspired by the microstructure of the embryonic cerebellum, we develop a new model of 2d morphogenesis in which system-spanning elastic fibers endow the organ with a preferred radius, while a separate fiber network resides in the otherwise fluid-like film at the outer edge of the organ and resists thickness gradients thereof. The tendency of the film to uniformly thicken or thin is described via a "growth potential". Several features of cerebellum, +blebbistatin organoid, and retinal fovea morphogenesis, including out-of-phase behavior and a film thickness amplitude that is comparable to the radius amplitude, are readily explained by our simple analytical model, as may be an observed scale-invariance in the number of folds in the cerebellum. We also study a nonlinear variant of the model, propose further biological and bio-inspired applications, and address how our model is and is not unique to the developing nervous system.Comment: version accepted by Physical Review

Transition Probabilities Of Astrophysical Interest In The Niobium Ions Nb+ And Nb2+

Aims. We attempt to derive accurate transition probabilities for astrophysically interesting spectral lines of Nb II and Nb III and determine the niobium abundance in the Sun and metal-poor stars rich in neutron-capture elements. Methods. We used the time-resolved laser-induced fluorescence technique to measure radiative lifetimes in Nb II. Branching fractions were measured from spectra recorded using Fourier transform spectroscopy. The radiative lifetimes and the branching fractions were combined yielding transition probabilities. In addition, we calculated lifetimes and transition probablities in Nb II and Nb III using a relativistic Hartree-Fock method that includes core polarization. Abundances of the sun and five metal-poor stars were derived using synthetic spectra calculated with the MOOG code, including hyperfine broadening of the lines. Results. We present laboratory measurements of 17 radiative lifetimes in Nb II. By combining these lifetimes with branching fractions for lines depopulating the levels, we derive the transition probabilities of 107 Nb II lines from 4d(3)5p configuration in the wavelength region 2240-4700 angstrom. For the first time, we present theoretical transition probabilities of 76 Nb III transitions with wavelengths in the range 1430-3140 angstrom. The derived solar photospheric niobium abundance log epsilon(circle dot) = 1.44 +/- 0.06 is in agreement with the meteoritic value. The stellar Nb/Eu abundance ratio determined for five metal-poor stars confirms that the r-process is a dominant production method for the n-capture elements in these stars.Integrated Initiative of Infrastructure RII3-CT-2003-506350Swedish Research CouncilKnut and Alice Wallenberg FoundationBelgian FRS-FNRSFRIAUS National Science Foundation AST-0607708, AST-0908978Astronom

EXPERIMENTALLY MEASURED RADIATIVE LIFETIMES AND OSCILLATOR STRENGTHS IN NEUTRAL VANADIUM

We report a new study of the V i atom using a combination of time-resolved laser-induced fluorescence and Fourier transform spectroscopy that contains newly measured radiative lifetimes for 25 levels between 24,648 cm−1 and 37,518 cm−1 and oscillator strengths for 208 lines between 3040 and 20000 Å from 39 upper energy levels. Thirteen of these oscillator strengths have not been reported previously. This work was conducted independently of the recent studies of neutral vanadium lifetimes and oscillator strengths carried out by Den Hartog et al. and Lawler et al., and thus serves as a means to verify those measurements. Where our data overlap with their data, we generally find extremely good agreement in both level lifetimes and oscillator strengths. However, we also find evidence that Lawler et al. have systematically underestimated oscillator strengths for lines in the region of 9000 ± 100 Å. We suggest a correction of 0.18 ± 0.03 dex for these values to bring them into agreement with our results and those of Whaling et al. We also report new measurements of hyperfine structure splitting factors for three odd levels of V i lying between 24,700 and 28,400 cm−1

Control of plant stem cell function by conserved interacting transcriptional regulators

Plant stem cells in the shoot apical meristem (SAM) and root apical meristem are necessary for postembryonic development of aboveground tissues and roots, respectively, while secondary vascular stem cells sustain vascular development. WUSCHEL (WUS), a homeodomain transcription factor expressed in the rib meristem of the Arabidopsis SAM, is a key regulatory factor controlling SAM stem cell populations, and is thought to establish the shoot stem cell niche through a feedback circuit involving the CLAVATA3 (CLV3) peptide signalling pathway. WUSCHEL-RELATED HOMEOBOX 5 (WOX5), which is specifically expressed in the root quiescent centre, defines quiescent centre identity and functions interchangeably with WUS in the control of shoot and root stem cell niches. WOX4, expressed in Arabidopsis procambial cells, defines the vascular stem cell niche. WUS/WOX family proteins are evolutionarily and functionally conserved throughout the plant kingdom and emerge as key actors in the specification and maintenance of stem cells within all meristems. However, the nature of the genetic regime in stem cell niches that centre on WOX gene function has been elusive, and molecular links underlying conserved WUS/WOX function in stem cell niches remain unknown. Here we demonstrate that the Arabidopsis HAIRY MERISTEM (HAM) family of transcription regulators act as conserved interacting cofactors with WUS/WOX proteins. HAM and WUS share common targets in vivo and their physical interaction is important in driving downstream transcriptional programs and in promoting shoot stem cell proliferation. Differences in the overlapping expression patterns of WOX and HAM family members underlie the formation of diverse stem cell niche locations, and the HAM family is essential for all of these stem cell niches. These findings establish a new framework for the control of stem cell production during plant development

The Sweat Lodge Ceremony as Experienced by Nurses A Hermeneutic Phenomenological Study

Nursing must reconnect with its roots found in the teachings of Florence Nightingale and be open to ancient indigenous wisdom, focusing on caring, healing and being present. To practice as culturally competent healers, nurses must grow in self awareness and an ability to understand cultural and spiritual practices, as well as communicate with and show respect to people from all walks of life. A Hermeneutic Phenomenological study was done by interviewing three participants to explore what it was like for Master in Arts nursing students participating in an Augsburg College Department of Nursing Immersion to experience a Sweat Lodge Ceremony; with data being analyzed in the context of nurse as healer. Seven major themes were found in analysis of the data: 1) Importance of being open, 2) Experienced elements of a therapeutic relationship/healing environment, 3) Sense of being connected,4) Healing experience, 5) Gained personal and cultural insights and growth, 6) Application to nursing practice, 7) Sweat Lodge Ceremony was a meaningful experience on a deeply personal level. Jean Watson\u27s Human Caring Theory served to guide, guard, connect and ground this study

Effect of thermal profile on cyclic flaw growth in aluminum

Surface flawed and single edge notch tension specimens of 2219-T851 and -T87 aluminum were tested to determine static fracture characteristics and base line (constant amplitude, constant temperature) cyclic flaw growth behavior. Subsequent testing was then conducted in which flawed specimens were subjected to a thermal profile in which the applied stress was varied simultaneously with the temperature. The profile used represents a simplified space shuttle orbiter load/temperature flight cycle. Test temperatures included the range from 144K (-200 F) up to 450K (350 F). The measured flaw growth rates obtained from the thermal profile tests were then compared with rates predicted by assuming linear cumulative damage of base line rates

Recruitment responses of benthic infauna to manipulated sediment geochemical properties in natural flows

Recent studies have shown that local variation in surface sediment geochemistry can have significant effects on recruitment rates of benthic invertebrates. Experiments presented here tested (1) the utility of manipulating surface porewater concentrations using spiked polyacrylamide gels and (2) the recruitment responses of the polychaete Arenicola cristata and the bivalve Mercenaria mercenaria to manipulated ammonium concentrations in realistic flows provided by a straight flume and an annular flume. Data show that successful manipulation of sediment porewater ammonium concentration is feasible in flowing waters, i.e., overlying waters remained relatively free of ammonium while manipulated concentration levels were maintained within the upper sediment layers where new recruits explore. Thus, over short experimental periods, ammonium signals can be independently modified while variables such as grain size, organic content and flow are held constant. Responses of new recruits varied as a function of experimental condition. In straight flume trials, the manipulation of ammonium concentration was successful, and within the range of concentrations tested, retention of Mercenaria was significantly reduced at the highest ammonium level. However, retention of Arenicola was uniformly low among all treatments and no significant ammonium response was detected. In annular flume runs, overall ammonium concentrations were higher than in straight flume runs, but were consistent with the intended manipulation. Mercenaria retention was uniformly low, and no differences in retention, as a function of ammonium concentration, were found. However, for Arenicola, significant differences were observed, with highest retention in lower ammonium environments. These results suggest that ammonium, isolated from other cues, plays a significant role in determining recruitment patterns, with variation in recruit responses related to signal strength