Cutting characteristics of dental diamond burs made with CVD technology Características de corte de pontas odontológicas diamantadas obtidas pela tecnologia CVD

The aim of this study was to determine the cutting ability of chemical vapor deposition (CVD) diamond burs coupled to an ultrasonic dental unit handpiece for minimally invasive cavity preparation. One standard cavity was prepared on the mesial and distal surfaces of 40 extracted human third molars either with cylindrical or with spherical CVD burs. The cutting ability was compared regarding type of substrate (enamel and dentin) and direction of handpiece motion. The morphological characteristics, width and depth of the cavities were analyzed and measured using scanning electron micrographs. Statistical analysis using the Kruskal-Wallis test (p < 0.05) revealed that the width and depth of the cavities were significantly greater when they were prepared on dentin. Wider cavities were prepared when the cylindrical CVD bur was used, and deeper cavities resulted from preparation with the spherical CVD bur. The direction of handpiece motion did not influence the size of the cavities, and the CVD burs produced precise and conservative cutting.<br>O objetivo deste estudo foi determinar a habilidade de corte das pontas de diamante obtidas pelo processo de deposição química a vapor (CVD) associadas ao aparelho de ultra-som no preparo cavitário minimamente invasivo. Uma cavidade padronizada foi preparada nas faces mesial e distal de 40 terceiros molares, utilizando-se pontas de diamante CVD cilíndrica e esférica. A habilidade de corte foi comparada quanto ao tipo de substrato (esmalte e dentina) e quanto à direção do movimento realizado com a ponta. As características morfológicas, a largura e profundidade das cavidades foram analisadas e medidas em microscopia eletrônica de varredura. A análise estatística pelo teste de Kruskal-Wallis (p < 0,05) revelou que a largura e profundidade das cavidades foram significativamente maiores em dentina. Cavidades mais largas foram obtidas quando se utilizou a ponta de diamante CVD cilíndrica, e mais profundas quando a ponta esférica foi empregada. A direção do movimento da ponta não influenciou o tamanho das cavidades, sendo os cortes produzidos pelas pontas de diamante CVD precisos e conservadores

In vitro evaluation of the effects of the interaction between irrigating solutions, intracanal medication and Er:YAG laser in dentin permeability of the endodontic system Estudo in vitro dos efeitos da interação de substâncias irrigantes, medicação intracanal e laser Er:YAG na permeabilidade dentinária do sistema endodôntico

The purpose of this study was to evaluate in vitro the effects of different associations between irrigating solutions (EDTA-T and citric acid), intracanal medicament (NDP), and Er:YAG laser irradiation on dentin permeability. Fifty-one extracted single-rooted teeth were instrumented and divided into seven groups. Groups GI and GII had final irrigation with a demineralizing solution only (EDTA-T and citric acid, respectively). Groups GIII and GIV had final irrigation with EDTA-T and citric acid, respectively, plus an association of irrigating solution and Er:YAG laser. Groups GV and GVI had final irrigation with EDTA-T and citric acid, respectively, plus an association of intracanal medication and Er:YAG laser. Group GVII (control group) had final irrigation with distilled water. All root canals were filled with NDP associated with rhodamine B dye. After the experimental period, the samples were transversely cut into six 2.0 mm thick slices for subsequent reading using the ImageLab software. Analysis of the results allowed us to conclude that there were statistically significant differences (p < 0.05) between the groups as to the penetration of the dye-intracanal medication solution. Groups III and IV presented smaller values of dentinal permeability when compared to the other groups. The best results were obtained with the interaction between a demineralizing irrigating solution and the association of intracanal medicament and laser Er:YAG (groups V and VI). In these groups the observed penetration of the intracanal medicament plus dye solution in the apical third was, on average, 29% greater than in the other groups.<br>Este experimento teve como objetivo avaliar in vitro os efeitos da interação entre soluções irrigantes desmineralizadoras (EDTA-T e ácido cítrico), medicação intracanal (NDP) e laser Er:YAG na permeabilidade dentinária. Foram utilizados 51 dentes unirradiculares extraídos que, após o preparo químico-cirúrgico, foram divididos em sete grupos experimentais: grupos I e II - irrigação final com solução de EDTA-T e ácido cítrico, respectivamente; grupos III e IV - irrigação final com EDTA-T e ácido cítrico, respectivamente, mais a associação entre solução irrigante e laser Er:YAG; grupos V e VI - irrigação final com EDTA-T e ácido cítrico, respectivamente, mais a associação entre medicação intracanal e laser Er:YAG, e grupo VII (controle) - irrigação final com água destilada. Os canais radiculares foram preenchidos com o corante rodamina B solubilizado na medicação de uso intracanal NDP. Após o período experimental, as amostras foram cortadas transversalmente para posterior leitura com o software ImageLab. A análise dos resultados permitiu concluir que existiram diferenças estatisticamente significantes (p < 0,05) quanto à penetração da solução corante-medicação intracanal nos diferentes grupos. Os grupos III e IV apresentaram menores valores de permeabilidade dentinária quando comparados aos outros e, finalmente, os melhores resultados foram obtidos quando da interação entre a solução irrigante desmineralizadora e a associação medicação intracanal/laser Er:YAG (grupos V e VI). Nesses, constatou-se que a diferença de penetração da solução corante-medicação intracanal no terço apical foi, em média, 29% maior do que nos demais grupos