Transition of chromium oxyhydroxide nanomaterials to chromium oxide: a hot-stage Raman spectroscopic study

The transition of disc-like chromium hydroxide nanomaterials to chromium oxide nanomaterials has been studied by hot stage Raman spectroscopy. The structure and morphology of α-CrO(OH) synthesised using hydrothermal treatment was confirmed by X-ray diffraction and transmission electron microscopy. The Raman spectrum of α-CrO(OH) is characterised by two intense bands at 823 and 630 cm-1 attributed to ν1 CrIII-O symmetric stretching mode, bands at 1179 cm-1 attributed to CrIII-OH δ deformation modes. No bands are observed above 3000 cm-1. The absence of characteristic OH vibrational bands may be due to short hydrogen bonds in the α-CrO(OH) structure. Upon thermal treatment of α-CrO(OH), new Raman bands are observed at 599, 542, 513, 396, 344 and 304 cm-1, which are attributed to Cr2O3. This hot-stage Raman study shows that the transition of α-CrO(OH) to Cr2O3 occurs before 350 °C

Особенности костного метаболизма при переломах костей таза в зависимости от пола и сопутствующего остеопороза у пострадавших

Костный метаболизм изучен у 85 больных с разными вариантами переломов костей таза, и у каждого пятого пациента регистрируется повышение уровня в крови остеоассоциированных макроэлементов — кальция и магния, у каждого девятого — фосфора, у 37 % от числа обследованных травмированных лиц — остеокальцина и у 57 % — активности щелочной фосфатазы. Нарушения костного метаболизма связаны с возрастом и полом пострадавших (в группе женщин чаще), определяют формирование остеопороза, влияют на тяжесть переломов, распространенность остеофрактур, характер переломов крестцовых, седалищных и лонных костей, а также оскольчатость последних.</jats:p