Enhanced critical current density of MgB2 superconductor synthesized in high magnetic fields

The effect of high magnetic fields on the current carrying properties of both MgB2 bulks and Fe-sheathed tapes was investigated following different thermal sequences. It is found that application of a large magnetic field during processing results in the quite uniform microstructure and the better connectivity between the MgB2 grains. As a result, the Jc of these samples has shown much higher value than that of the MgB2 samples in the absence of magnetic field. The possible mechanism of the Jc enhancement under an external magnetic field is also discussed.Comment: Presented at ISS2005, Tsukuba, 24-26 Oct., 2005; Revised versio

Development of Powder-in-Tube Processed Iron Pnictide Wires and Tapes

The development of the PIT fabrication process of iron pnictide superconducting wires and tapes has been carried out in order to enhance their transport properties. Silver was found to be the best sheath material, since no reaction layer was observed between the silver sheath and the superconducting core. The grain connectivity of iron pnictide wires and tapes has been markedly improved by employing Ag or Pb as dopants. At present, critical current densities in excess of 3750 A/cm^2 (Ic = 37.5 A) at 4.2 K have been achieved on Ag-sheathed SrKFeAs wires prepared with the above techniques, which is the highest in iron-based wires and tapes so far. Moreover, Ag-sheathed Sm-1111 superconducting tapes were successfully prepared by PIT method at temperatures as low as 900C, instead of commonly used temperatures of 1200C. These results demonstrate the feasibility of producing superconducting pnictide composite wires, even grain boundary properties require much more attention.Comment: 4 pages, 6 figures. Submitted to ASC2010 proceeding